| Specification | ASTM A 193/ASME SA 193 |
| Standard | all International Standards and ASTM, DIN, BS |
| Size | M3 - M56 | 3/6" to 2" | Custom Sizes |
| Length | 3 mm to 200 mm | Custom Sizes |
| Dimensions | DIN 931, 933, 934, 7991, 976, 125, ASME B18.2.1, B18.3 |
| Form | Hex, Threading, Square, Round as per Gauge Etc. |
| Threads | Unless otherwise specified, the threads shall be rolled or cut and tapped horizontally or vertically |
| Threads available | UNF, BSW, BSF, METRIC, UNC, or as required |
| Threads Configuration |
ASME B1.1 2A/3A – 2B/3B Inch Unified Threads and B1.13M 6h-6G Metric Coarse Threads |
| Certification | Dual Certified As per ASTM & ASME Codes |
| Test Certificate | As per EN 10204 / 3.1 Manufacturer Test Certificate, PED 97/23/EC Certified, Merkblatt AD 2000 W2 Certified |
| Raw materials Source | JSPL, Mukund Steel, Tata Steel, Dhamm Steel, Usha Martin,etc. |
| Packing | IN BULK: canton, pallet, Small Boxs / carton / pallet, or customer request |
| Surface Coating |
Cadmium Coating Hot Dipped Galvanizing Coating Ptfe Coated Phosphate Coating Teflon Coating Xylon Coating Zinc Coating |
| STANDARD | WERKSTOFF NR. | UNS | JIS | GOST | EN | OR |
| Hastelloy B2 | 2.4617 | N10665 | NW 0665 | - | - | - |
| Hastelloy B3 | 2.4600 | N10675 | - | - | - | - |
| Hastelloy X | 2.4665 | N06002 | - | - | - | - |
| Grade | C | Mn | Si | S | Co | Ni | Cr | Fe | Mo | P | Hastelloy B2 | 0.02 max | 1.0 max | 0.1 max | 0.03 max | 1.0 max | Bal | 1.0 max | 2.0 max | 26 – 30 | 0.04 max |
| Hastelloy B3 | 0.01 max | 3.0 max | 0.10 max | - | 3.0 max | 65.0 min | 1.5 max | 1.5 max | 27.0-32.0 | - |
| Hastelloy X | 0.05-0.15 | 1.0 max | 1.0 max | - | 0.5-2.5 | Balance | 20.5-23.0 | 17.0-20.0 | 8.0-10.0 | - |
| Element | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| Hastelloy B2 | 9.2 g/cm3 | 1370 °C (2500 ºF ) | Psi – 1,10,000 , MPa – 760 | Psi – 51000 , MPa – 350 | 40 % |
| Hastelloy B3 | 9.22 g/cm3 | 1418 °C | 1000-2000 MPa | 350 MPa | 40% |
| Hastelloy X | 9.2 g/cm3 | 1370 °C (2500 °F) | Psi – 51,000, MPa – 350 | Psi -1,10,000, MPa -760 | 40 % |