The Hastelloy C22 Anchor Bolts contain various elements in their chemical composition. These elements include molybdenum and tungsten, along with nickel and chromium. These Hastelloy Anchor Bolts provide resistance towards corrosion and its related damages. These Anchor Bolts also show excellent performance in environments that are subjected to various acids such as formic acid, acetic acid, and so on. Hastelloy C276 Anchor Bolts also have a chemical composition that includes nickel, molybdenum & chromium. It also has tungsten in its chemical composition. The presence of this element in the composition makes the Anchor Bolts more resistant towards corrosion.
The Hastelloy B2 Anchor Bolts also provide resistance towards acids such as sulfuric acid, phosphoric acid, and hydrochloric acid. There also is iron along with chromium in its chemical composition, which offers excellent fabricability. Hastelloy UNS N06002 Anchor Bolts also have the property of durability. Also, these undergo a series of tests to test and improve their quality. The Hastelloy X Anchor Bolts also have resistance towards oxidation. They also have the property of fabricability.
| Specification | ASTM F593, F594, F1554 / ASME SF593, F594, F1554 |
| Standard |
DIN : DIN 934, DIN 931, DIN 970, DIN 933 UTS : UNEF, NPT, UNC, UNS, UNF, NPTF ISO : JIS standards, ISO 4033, ISO 4032, ANSI – American National Standards Institute ASME B18.5 ANSI B 28.2.4 1M as per defined in ASME B16.5 standard Hastelloy® Alloy C276 Stud Nuts length ANSI B 18.2.4 2M as per defined in ASME B18.2.2 Hastelloy Alloy C276 Hex nuts |
| Size | M3 - M56 | 3/6" to 2" | Custom Sizes |
| Length | 3 mm to 200 mm | Custom Sizes |
| Dimensions | DIN 931, 933, 934, 7991, 976, 125, ASME B18.2.1, B18.3 |
| Form | Hex, Threading, Square, Round as per Gauge Etc. |
| Threads | Unless otherwise specified, the threads shall be rolled or cut and tapped horizontally or vertically |
| Threads available | UNF, BSW, BSF, METRIC, UNC, or as required |
| Threads Configuration |
ASME B1.1 2A/3A – 2B/3B Inch Unified Threads and B1.13M 6h-6G Metric Coarse Threads |
| Certification | Dual Certified As per ASTM & ASME Codes |
| Test Certificate | As per EN 10204 / 3.1 Manufacturer Test Certificate, PED 97/23/EC Certified, Merkblatt AD 2000 W2 Certified |
| Raw materials Source | JSPL, Mukund Steel, Hilti India Tata Steel, Dhamm Steel, Usha Martin,etc. |
| Packing | IN BULK: canton, pallet, Small Boxs / carton / pallet, or customer request |
| Surface Coating |
Cadmium Coating Hot Dipped Galvanizing Coating Ptfe Coated Phosphate Coating Teflon Coating Xylon Coating Zinc Coating |
| STANDARD | WERKSTOFF NR. | UNS | JIS | GOST | EN | OR |
| Hastelloy C22 | 2.4602 | N06022 | NW 6022 | - | NiCr21Mo14W | - |
| Hastelloy C276 | 2.4819 | N10276 | NW 0276 | ХН65МВУ | NiMo16Cr15W | ЭП760 |
| Hastelloy B2 | 2.4617 | N10665 | NW 0665 | - | - | - |
| Hastelloy B3 | 2.4600 | N10675 | - | - | - | - |
| Hastelloy X | 2.4665 | N06002 | - | - | - | - |
| Grade | C | Mn | Si | S | Co | Ni | Cr | Fe | Mo | P |
| C22 | 0.010 max | 0.50 max | 0.08 max | 0.02 max | 2.5 max | Bal | 20 - 22.5 | 2 – 6 | 12.5 – 14.5 | 0.02 max |
| C276 | 0.010 max | 1.00 max | 0.08 max | 0.03 max | 2.50 max | 50.99 min* | 14.50 – 16.50 | 4.00 – 7.00 | 15.00 – 17.00 | 0.04 max |
| Hastelloy B2 | 0.02 max | 1.0 max | 0.1 max | 0.03 max | 1.0 max | Bal | 1.0 max | 2.0 max | 26 – 30 | 0.04 max |
| Hastelloy B3 | 0.01 max | 3.0 max | 0.10 max | - | 3.0 max | 65.0 min | 1.5 max | 1.5 max | 27.0-32.0 | - |
| Hastelloy X | 0.05-0.15 | 1.0 max | 1.0 max | - | 0.5-2.5 | Balance | 20.5-23.0 | 17.0-20.0 | 8.0-10.0 | - |
| Element | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| Hastelloy C22 | 8.69 g/cm3 | 1399 °C (2550 °F) | Psi – 1,00,000 , MPa – 690 | Psi – 45000 , MPa – 310 | 45% |
| Hastelloy C276 | 8.89 g/cm3 | 1370 °C (2500 °F) | Psi – 1,15,000 , MPa – 790 | Psi – 52,000 , MPa – 355 | 40 % |
| Hastelloy B2 | 9.2 g/cm3 | 1370 °C (2500 ºF ) | Psi – 1,10,000 , MPa – 760 | Psi – 51000 , MPa – 350 | 40 % |
| Hastelloy B3 | 9.22 g/cm3 | 1418 °C | 1000-2000 MPa | 350 MPa | 40% |
| Hastelloy X | 9.2 g/cm3 | 1370 °C (2500 °F) | Psi – 51,000, MPa – 350 | Psi -1,10,000, MPa -760 | 40 % |